物理性能额定值单位制测试方法比重1.04g/cm³ASTM D792熔流率（熔体流动速率） (220°C/10.0 kg)23g/10 minASTM D1238收缩率 - 流动 (3.20 mm)0.40 到 0.70%ASTM D955Dimensio
nal Stability0.0%ASTM D1042硬度额定值单位制测试方法洛氏硬度 (R 级)110ASTM D785机械性能额定值单位制测试方法拉伸模量 1(3.20 mm)2220MPaASTM D638抗张强度 2(屈服, 3.20 mm)51.0MPaASTM D638伸长率 3(断裂, 3.20 mm)30%ASTM D638弯曲模量 4(3.20 mm)2750MPaASTM D790弯曲强度 5(3.20 mm)78.5MPaASTM D790冲击性能额定值单位制测试方法悬壁梁缺口冲击强度ASTM D256 -30°C, 3.20 mm78J/mASTM D256 -30°C, 6.40 mm78J/mASTM D256 23°C, 3.20 mm230J/mASTM D256 23°C, 6.40 mm200J/mASTM D256热性能额定值单位制测试方法载荷下热变形温度ASTM D648 0.45 MPa, 未退火, 6.40 mm90.0°CASTM D648 1.8 MPa, 未退火, 6.40 mm86.0°CASTM D648维卡软化温度94.0°CASTM D1525RTI ElecUL 746 1.50 mm95.0°CUL 746 3.00 mm100°CUL 746RTI ImpUL 746 1.50 mm95.0°CUL 746 3.00 mm100°CUL 746RTIUL 746 1.50 mm95.0°CUL 746 3.00 mm100°C