物性性能测试条件测试方法测试结果测试单位密度ASTM D792/ISO 11830.918熔融指数（流动系数）ASTM D1238/ISO 11332.0g/10min物理性能测试条件测试方法测试结果测试单位光泽度60℃ASTM D-245760混浊ASTM D-100315%机械性能测试条件测试方法测试结果测试单位断裂伸长率MDASTM D-882700%断裂伸长率TDASTM D-882750%抗穿刺强度SABIC63J/mm落锤冲击ASTM D-1709110g1%割线模量MD，1%ASTM D-882220Mpa1%割线模量TD，1%ASTM D-882260Mpa门氏撕裂强度MDASTM D-1922135g门氏撕裂强度TDASTM D-1922400g断裂拉伸强度MDASTM D-88235Mpa断裂拉伸强度TDASTM D-88259Mpa屈服拉伸强度MDASTM D-88212Mpa屈服拉伸强度TDASTM D-88210Mpa断裂伸长率ASTM D638/ISO 527750%拉伸强度ASTM D638/ISO 52759kg/cm²(MPa)[Lb/in²]弯曲强度ASTM D790/ISO 17810kg/cm²(MPa)[Lb/in²]基本性能测试条件测试方法测试结果测试单位熔融指数ASTM D-12382.0g/10min密度ASTM D-7920.918g/cm