物理性能额定值单位测试方法比重0.902g/cm³ASTM D792熔流率 (190℃/2.16 kg)1.0g/10 minASTM D1238薄膜额定值单位测试方法薄膜厚度 (经测试)51µm膜刺穿强度 (51 µm)8.81JInternal Method膜刺穿力 (51 µm)82.5NInternal Method膜耐刺穿性 (51 µm)22.3J/cm³Internal Method割线模量 (2% 正割, MD : 51 µm)91.7MPaASTM D882(2% 正割, TD : 51 µm)92.4MPaASTM D882抗张强度 (MD : 屈服, 51 µm)7.24MPaASTM D882 (TD : 屈服, 51 µm)6.89MPaASTM D882 (MD : 断裂,51 µm)58.6MPaASTM D882 (TD : 断裂,51µm)44.7MPaASTM D882伸长率 (MD : 断裂, 51 µm)620%ASTM D882(TD : 断裂, 51 µm)630%ASTM D882落锤冲击 (51 µm)> 830gASTM D1709B埃尔曼多夫抗撕强度 (MD : 51 µm)550gASTM D1922(TD : 51 µm)720gASTM D1922始封温度 (51 µm)85.0℃Internal Method热性能额定值单位测试方法维卡软化温度86.0℃ASTM D1525溶融温度 (DSC)99.0℃Internal Method光学性能额定值单位测试方法光泽度 (20°, 50.8 µm)141ASTM D2457透明度 (50.8 µm)83.0ASTM D1746雾度 (50.8 µm)1.1%ASTM D1003