物性性能测试条件测试方法测试结果测试单位熔融指数（流动系数）ASTM D1238/ISO 11331.6g/10min熔融指数（流动系数）ASTM D1238/ISO 113323g/10min密度ASTM D792/ISO 11831.05机械性能测试条件测试方法测试结果测试单位拉伸强度ASTM D638/ISO 527490(6,950)kg/cm²(MPa)[Lb/in²]伸长率ASTM D638/ISO 52720%洛氏硬度ASTM D785R-116弯曲模量ASTM D790/ISO 17827000(38000)kg/cm²(MPa)[Lb/in²]弯曲强度ASTM D790/ISO 178790(11,660)kg/cm²(MPa)[Lb/in²]IZOD 缺口冲击强度ASTM D256/ISO 17920(3.7)kg·cm/cm(J/M)ft·lb/inIZOD 缺口冲击强度ASTM D256/ISO 17917(3.1)kg·cm/cm(J/M)ft·lb/in热性能测试条件测试方法测试结果测试单位燃烧性（率）UL941.6mmHB热变形温度ASTM D648/ISO 7599(210)℃（℉）热变形温度ASTM D648/ISO 7588(190)℃（℉）维卡软化点ASTM D1525/ISO R306105(221)℃（℉）加工性能测试条件测试方法测试结果测试单位干燥条件80°C下烘料约2~3小时加工温度180~220°C加工温度190~230°C加工温度180~230°C°C模具温度30~70°C°C