基本性能额定值单位测试方法熔体流动速率45g/10minASTM D1238 (190℃/2.16kg)45g/10minISO 1133吸水率 (24 hr)0.2%ASTM D570物理性能额定值单位测试方法比重1.41g/cmASTM D792,ISO 1183成型收缩率 (Flow)1.6-2%ASTM D955,ISO 294-4 (Across Flow)1.6-2%ISO 294-4洛氏硬度ASTM D785 (M-Scale)80 (R-Scale)115机械性能额定值单位测试方法拉伸模量2900MPaISO 527-2屈服拉伸应力67MPaISO 527-2拉伸应力61MPaASTM D638断裂伸长率45%ASTM D63830%ISO 527-2弯曲模量2630MPaASTM D790弯曲强度90MPaASTM D790泰伯耐磨性 (1000 Cycles)14mgASTM D1044CHARPY缺口冲击强度 (23℃)4.5kJ/mISO 179/1eAIzod 缺口冲强度39J/mASTM D256热性能额定值单位测试方法热变形温度 (0.45MPa,unannealed)158℃ASTM D648 (0.45MPa,unannealed)156℃ISO 75-2/B (1.8MPa,unannealed)110℃ASTM D648 (1.8MPa,unannealed)105℃ISO 75-2/A流动方向线性热膨胀系数0.0001cm/cm/℃ASTM E831阻燃等级HBUL 94