TAISOX 3224 物性表基本信息添加剂中等抗结块性中度光滑性特性低密度良好的剥离性良好的热封性中等抗结块性用途薄膜拉伸缠绕形式粒子加工方法吹塑薄膜物理性能额定值单位制测试方法密度0.920g/cm³ASTM D1505熔流率（熔体流动速率） (190°C/2.16 kg)2.0g/10 minASTM D1238薄膜额定值单位制测试方法薄膜厚度 - 经测试38µm割线模量ASTM D882 1% 正割, MD : 38 µm, 吹塑薄膜147MPaASTM D882 1% 正割, TD : 38 µm, 吹塑薄膜206MPaASTM D882抗张强度ASTM D882 MD : 屈服, 38 µm, 吹塑薄膜9.81MPaASTM D882 TD : 屈服, 38 µm, 吹塑薄膜10.8MPaASTM D882 MD : 断裂, 38 µm, 吹塑薄膜35.3MPaASTM D882 TD : 断裂, 38 µm, 吹塑薄膜27.5MPaASTM D882伸长率ASTM D882 MD : 断裂, 38 µm, 吹塑薄膜600%ASTM D882 TD : 断裂, 38 µm, 吹塑薄膜800%ASTM D882落锤冲击 (38 µm, 吹塑薄膜)120gASTM D1709埃尔曼多夫抗撕强度ASTM D1922 MD : 38 µm, 吹塑薄膜61gASTM D1922 TD : 38 µm, 吹塑薄膜650gASTM D1922热性能额定值单位制测试方法脆化温度-70.0°CASTM D746维卡软化温度93.0°CASTM D1525熔融温度122°C光学性能额定值单位制测试方法光泽度 (45°, 38.0 µm, 吹塑薄膜)47ASTM D2457透明度53.0ASTM D1746雾度 (38.0 µm, 吹塑薄膜)24%ASTM D1003补充信息Blow Up Ratio: 2