物理性能额定值 (公制)额定值 (英制)测试方法比重1.34 g/cc1.34 g/ccASTM D 792吸水率0.080 %@Time 86400 sec0.080 %@Time 24.0 hourASTM D 570线性模具收缩，Flow0.0080 - 0.011 cm/cm@Thickness 0.750 - 2.30 mm0.0080 - 0.011 in/in@Thickness 0.0295 - 0.0906 inSABIC Method0.010 - 0.014 cm/cm@Thickness 2.30 - 4.60 mm0.010 - 0.014 in/in@Thickness 0.0906 - 0.181 inSABIC Method线性成型收缩率，横向0.0090 - 0.013 cm/cm@Thickness 0.750 - 2.30 mm0.0090 - 0.013 in/in@Thickness 0.0295 - 0.0906 inSABIC Method机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（R 级）117117ASTM D 785抗张强度(断裂)48.0 MPa6960 psiType I, 50 mm/min; ASTM D 638抗张强度(屈服)48.0 MPa6960 psiType I, 50 mm/min; ASTM D 638伸长率 (断裂)110 %110 %Type I, 50 mm/min; ASTM D 638弯曲强度82.0 MPa11900 psi1.3 mm/min, 50 mm span; ASTM D 79082.0 MPa11900 psi1.3 mm/min, 50 mm span; ASTM D 790弯曲模量2.06 GPa299 ksi1.3 mm/min, 50 mm span; ASTM D 790悬壁梁缺口冲击强度5.30 J/cm@Temperature 23.0 °C9.93 ft-lb/in@Temperature 73.4 °FASTM D 256悬壁梁无缺口冲击强度32.02 J/cm@Temperature 23.0 °C59.99 ft-lb/in@Temperature 73.4 °FASTM D 4812Gardner Impact43.0 J@Temperature 23.0 °C31.7 ft-lb@Temperature 73.4 °FASTM D 302943.0 J@Temperature 23.0 °CASTM D 3029电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率>= 1.20e+16 ohm-cm>= 1.20e+16 ohm-cmASTM D 257介电常数3.2@Frequency 100 Hz3.2@Frequency 100 HzASTM D 1503.2@Frequency 1.00e+6 Hz3.2@Frequency 1.00e+6 HzASTM D 150介电强度18.5 kV/mm@Thickness 3.20 mm470 kV/in@Thickness 0.126 inin air; ASTM D 14918.5 kV/mm@Thickness 3.20 mmin oil; ASTM D 14925.1 kV/mm@Thickness 1.60 mm638 kV/in@Thickness 0.0630 inin oil; ASTM D 149耗散因数0.0030@Frequency 100 Hz0.0030@Frequency 100 HzASTM D 1500.030@Frequency 1.00e+6 Hz0.030@Frequency 1.00e+6 HzASTM D 150耐电弧性60 - 120 sec60 - 120 secTungsten, PLC code 6; ASTM D 495相比耐漏电起痕指数(CTI)VVPLC code 2; UL 746A热丝引燃 (HWI)30 - 60 sec30 - 60 secPLC code 2; UL 746A高电弧燃烧，HAI15 - 30 arcs15 - 30 arcssurface, PLC code 3; UL 746A高压电弧跟踪率，HVTR80.0 - 150 mm/min- 5.91 in/minPLC code 3; UL 746A热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动91.8 µm/m-°C@Temperature -40.0 - 40.0 °C51.0 µin/in-°F@Temperature -40.0 - 104 °FASTM E 831124 µm/m-°C@Temperature 60.0 - 138 °C68.9 µin/in-°F@Temperature °FASTM E 831载荷下热变形温度(0.46 MPa)137 °C@Thickness 6.40 mm279 °F@Thickness 0.252 inunannealed; ASTM D 648载荷下热变形温度(1.8 MPa)98.0 °C@Thickness 6.40 mm208 °F@Thickness 0.252 inunannealed; ASTM D 648UL RTI120 °C248 °FUL 746BUL RTI，机械冲击120 °C248 °FUL 746BUL RTI，机械无冲击140 °C284 °FUL 746B可燃性(UL94)HB@Thickness 0.450 mmHB@Thickness 0.0177 inUL 94 by SABIC-IPV-0@Thickness 0.630 mmV-0@Thickness 0.0248 inUL 94 by SABIC-IP5VA@Thickness 2.99 mm5VA@Thickness 0.118 inUL 94 by SABIC-IP