PA66 FR72G25 V0 杜邦 PA66--25% Glass Reinforced Flame Retardant Polyamide 66
Zytel FR70G25V0 NC010 is a 25% glass fiber reinforced heat stabilized flame retardant polyamide 66 resin for injection molding.
25%玻璃增强阻燃聚酰胺66
Zytel FR70G25V0 NC010是一种用于注塑成型的25%玻璃纤维增强热稳定阻燃聚酰胺66树脂。
PA66 FR72G25 V0物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.35 g/cc | 0.0488 lb/in³ | |
| 1.49 g/cc | 0.0538 lb/in³ | DAM; ISO 1183 | |
| 吸水率 | 3.4 % @Thickness 2.00 mm | 3.4 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | 0.900 % @Thickness 2.00 mm | 0.900 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 粘度 | 85370 cP @Shear Rate 5000 1/s, Temperature 280 °C | 85370 cP @Shear Rate 5000 1/s, Temperature 536 °F | ISO 11403-1 -2 |
| 138900 cP @Shear Rate 5000 1/s, Temperature 270 °C | 138900 cP @Shear Rate 5000 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| 243400 cP @Shear Rate 5000 1/s, Temperature 260 °C | 243400 cP @Shear Rate 5000 1/s, Temperature 500 °F | ISO 11403-1 -2 | |
| 270750 cP @Shear Rate 500 1/s, Temperature 280 °C | 270750 cP @Shear Rate 500 1/s, Temperature 536 °F | ISO 11403-1 -2 | |
| 441600 cP @Shear Rate 500 1/s, Temperature 270 °C | 441600 cP @Shear Rate 500 1/s, Temperature 518 °F | ISO 11403-1 -2 | |
| 774800 cP @Shear Rate 500 1/s, Temperature 260 °C | 774800 cP @Shear Rate 500 1/s, Temperature 500 °F | ISO 11403-1 -2 | |
| 粘度测试 | 140 cm³/g | 140 cm³/g | DAM; ISO 307 1157 1628 |
| 线性成型收缩率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 线性成型收缩率，横向 | 0.010 cm/cm | 0.010 in/in | DAM; ISO 294-4 2577 |