| 比重 | 0.924 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率）(190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| 抗环境应力开裂(50°C, **** Igepal, F50) | 20.0 | hr | ASTM D1693 |
| 肖氏硬度(邵氏 D) | 50 | ASTM D2240 |
| 抗张强度 | ASTM D638 | ||
| 屈服 | 11.7 | MPa | ASTM D638 |
| 断裂 | 7.58 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服 | 3.0 | % | ASTM D638 |
| 断裂 | 60 | % | ASTM D638 |
| 弯曲模量 - 2% 正割 | 386 | MPa | ASTM D790B |
| 拉伸冲击强度1 | 168 | kJ/m2 | ASTM D1822 |
| 载荷下热变形温度(0.45 MPa, 未退火) | 42.8 | °C | ASTM D648 |
| 脆化温度 | -76.1 | °C | ASTM D746 |
| 维卡软化温度 | 93.9 | °C | ASTM D1525 |
| 溶融温度（DSC） | 123 | °C | 内部方法 |
| 结晶峰温度 (DSC) | 108 | °C | 内部方法 |