TPU 德国巴斯夫收缩率测试——上海溉邦实业有限公司UE-80A~UE-90A1.5~1.7 UE-95A~UE-71D0.8~1.2 UTX95A3.3 UTX-60D~UTX-71D2.1~2.6 UTY-85A~UTY-95A2.9~3.7 UTY-98A~UTY-60D2.3~2.5 UTY-64D~UTY-71D1.9~2.2 UTC-85A~UTC-90A3.7~3.9 UTC-95A~UTC-98A2.5~3.0 UTC-60D~UTC-64D2.1~2.3 US-60A~US-70A2.5~2.6物性表机械性能测试条件测试方法测试结果单位抗拉模数****DIN 53504-S211N/mm断裂延伸率DIN 53504-S2550%室温压缩变形率DIN 5351725%抗拉强度DIN 53504-S250N/mm撕裂强度DIN 53515120N/mm磨擦损耗DIN 5351630mm抗拉模数300%DIN 53504-S220N/mm凹凸冲击强度＋23℃DIN 53453不破裂KJ/m硬度DIN 5350548Shore D凹凸冲击强度－30℃DIN 534536KJ/m硬度DIN 5350596shoreA抗拉模数20%DIN 53504-S28N/mm****模量ASTM D412/ISO 5272Mpa/Psi300%模量ASTM D412/ISO 5274Mpa/Psi抗张强度ASTM D412/ISO 52730Mpa/Psi撕裂强度ASTM D624/ISO 3435n/mm²硬度 AASTM D2240/ISO 86860Shore A基本性能测试条件测试方法测试结果单位密度DIN 534791.24g/cm