物性性能测试条件测试方法测试结果单位密度ASTM D792/ISO 11830.954成型收缩率ASTM D9553.5%熔融指数(流动系数)ASTM D1238/ISO 113329g/10minASTM D1238/ISO 11330.35g/10min吸水率 23℃/24HASTM D570/ISO 620.002%机械性能测试条件测试方法测试结果单位断裂伸长率ASTM D638/ISO 527450%拉伸模量ASTM D638/ISO 5271500kg/cm²(MPa)[Lb/in²]拉伸强度ASTM D638/ISO 52727kg/cm²(MPa)[Lb/in²]伸长率ASTM D638/ISO 527500%洛氏硬度ASTM D78562拉伸断裂伸长率(延伸率)ASTM D638/ISO 527500%热性能测试条件测试方法测试结果单位热变形温度ASTM D648/ISO 75102℃(℉)加工性能测试条件测试方法测试结果单位干燥条件90加工温度220°C200°C210°C190°C模具温度210°C熔体温度190°C