EAA美国陶氏5980I物性表 EAA 美国陶氏 5980I 热融级物理性能测试条件测试方法测试结果单位熔体质量流动速率125°C/2.16kg2ASTMD1238,ISO113314g/10min190°C/2.16kg3ASTMD1238,ISO1133300g/10min共聚单体含量4内部方法20.5%机械性能测试条件测试方法测试结果单位拉伸模量-2%正割模压成型ASTMD638,ISO527-233.1Mpa抗张强度断裂,模压成型ASTMD638,ISO527-29.65Mpa伸长率断裂,模压成型ASTMD638,ISO527-2390%邵氏硬度Shore DASTM D-2240Shore DISO 868拉伸模量-2% SecantCompression MoldedMPaASTM D-63833.1Compression MoldedMPaISO 527-233.1拉伸断裂强度Compression MoldedMPaASTM D-6389.65Compression MoldedMPaISO 527-29.65拉伸断裂伸长率Compression Molded%ASTM D-638390Compression Molded%ISO 527-2390热性能测试条件测试方法测试结果单位维卡软化点℃ASTM D-152542.2℃ISO 30642.2熔融温度℃Internal Method77.2维卡软化温度ASTMD1525,ISO30642.2°C溶融温度（DSC）内部方法77.2°C硬度测试条件测试方法测试结果单位肖氏硬度邵氏DASTMD2240,ISO86850基本性能测试条件测试方法测试结果单位熔融指数125℃/2.16kgg/10minASTM D-1238190℃/2.16kgg/10minISO 1133300单体含量%Internal Method20.5熔融指数190℃/2.16kgg/10minASTM D-℃/2.16kgg/10minISO 1133