EAA原包料批发价#EAA 1321 美国盛禧奥（斯泰隆）
物理性能测试条件测试方法测试结果单位密度 / 比重g/cm³ASTM D-7920.935
g/cm³ISO 1183/A0.935共聚单体含量3
内部方法6.5%熔体质量流动速率2190°C/2.16kgASTMD1238,ISO11332.6g/10min密度 / 比重
ASTMD792,ISO1183/A0.935g/cm³机械性能测试条件测试方法测试结果单位伸长率断裂,模压成型ISO527-2/508640%断裂,模压成型4ASTMD638640%抗张强度断裂,模压成型ISO527-2/50820.1Mpa断裂,模压成型4ASTMD63820.1Mpa屈服,模压成型ISO527-2/50810.0Mpa屈服,模压成型4ASTMD63810.0Mpa拉伸屈服强度Compression MoldedMPaASTM D-63810Compression MoldedMPaISO 527-2/50810拉伸断裂强度Compression MoldedMPaASTM D-63820.1拉伸断裂强度(TD)50.8umMPaISO 527-331.8拉伸断裂强度(MD)50.8umMPaISO 527-331.8拉伸断裂伸长率(TD)50.8um%ASTM D-882510拉伸断裂伸长率(MD)50.8um%ASTM D-88246050.8um%ISO 527-3460拉伸断裂伸长率(TD)50.8um%ISO 527-3510落锤冲击50.8umgASTM D-1709B41050.8umgISO 7765-1/B410埃尔曼多夫撕裂强度(MD)50.8umgASTM D-1922270埃尔曼多夫撕裂强度(TD)50.8umgASTM D-1922390拉伸断裂强度Compression MoldedMPaISO 527-2/50820.1拉伸断裂伸长率Compression Molded%ASTM D-638640Compression Molded%ISO 527-2/508640薄膜厚度-Tested
um
50.8拉伸屈服强度(MD)50.8umMPaASTM D-88211.3拉伸屈服强度(TD)50.8umMPaASTM D-88211.1拉伸屈服强度(MD)50.8umMPaISO 527-311.3拉伸屈服强度(TD)50.8umMPaISO 527-311.5拉伸断裂强度(TD)50.8umMPaASTM D-88231.8拉伸断裂强度(MD)50.8umMPaASTM D-88231.8埃尔曼多夫撕裂强度(MD)50.8umNISO 埃尔曼多夫撕裂强度(TD)50.8umNISO 光学性能测试条件测试方法测试结果单位光泽度45°，50.8um
ASTM D-245776雾度（Haze）50.8um%ASTM D-um%ISO 147823.7光泽度45°,50.8µmASTMD245776
雾度（Haze）50.8µmISO147823.7%50.8µmASTMD10033.7%热性能测试条件测试方法测试结果单位维卡软化点
℃ASTM D-152588.9
℃ISO 30688.9熔化温度
℃DSC103维卡软化温度
ASTMD1525,ISO30688.9°C溶融温度（DSC）
内部方法103°C薄膜测试条件测试方法测试结果单位埃尔曼多夫抗撕强度5TD:51µmASTMD1922390gMD:51µmISONTD:51µmISON抗张强度MD:屈服,51µmASTMD88211.3MpaTD:屈服,51µmASTMD88211.1MpaMD:屈服,51µmISO527-311.3MpaTD:屈服,51µmISO527-311.5MpaMD:断裂,51µmASTMD882,ISO527-331.8MpaTD:断裂,51µmASTMD882,ISO527-331.8Mpa伸长率MD:断裂,51µmASTMD882,ISO527-3460%TD:断裂,51µmASTMD882,ISO527-3510%落锤冲击51µmASTMD1709B,ISO7765-1/B410g埃尔曼多夫抗撕强度5MD:51µmASTMD1922270g加工性能测试条件测试方法测试结果单位熔体温度
℃
193基本性能测试条件测试方法测试结果单位熔体流动速率190℃/2.16kgg/10minASTM D-℃/2.16kgg/10minISO 11332.6单体含量
%Internal Method6.5