物性表物性纠错物性性能测试条件测试方法测试结果单位密度ASTM D792/ISO 11831.42熔融指数(流动系数)ASTM D1238/ISO 113339g/10min吸水率 23℃/24HASTM D570/ISO 620.2%物理性能测试条件测试方法测试结果单位吸水率ASTM D5700.2%缩模率-,平行方向1.7-2.1%-,垂直方向1.7-2.1%机械性能测试条件测试方法测试结果单位拉伸强度ASTM D63870Mpa延伸率ASTM D63830%弯曲强度ASTM D790108Mpa弯曲模量ASTM D7903040MpaIZOD缺口冲击强度ASTM D25649J/m洛氏硬度ASTM D78594MASTM D785120R磨耗ASTM D104413拉伸强度ASTM D638/ISO 52770kg/cm²(MPa)[Lb/in²]洛氏硬度ASTM D78594弯曲模量ASTM D790/ISO 1783040kg/cm²(MPa)[Lb/in²]弯曲强度ASTM D790/ISO 178108kg/cm²(MPa)[Lb/in²]热性能测试条件测试方法测试结果单位燃烧性(率)UL94HB热变形温度ASTM D648/ISO 75136℃(℉)熔融指数ASTM D123839g/10min线膨胀系数10热变形温度-,1.82MPaASTM D648136°C-,0.45MPaASTM D648172°C阻燃性UL94HB