商品描述价格说明联系我们规格25加工定制否有效成分含量15％ 玻璃纤维增强材料产地美国品名聚对苯二甲酸乙二酯是否进口是厂家(产地)美国杜邦牌号FR543NC加工级别注塑级特性级别阻燃级用途级别纤维销售方式品牌经销类型标准料货号11026品牌RyniteDuPont Performance Polymers Rynite® FR543 NC010 PETPolyethylene Terephthalate (PET), 40% Glass ReinforcedDuPont Performance Polymers产品说明：Rynite® FR543 NC010 is a flame retardant, 43% glass reinforced polyethylene terephthalate. Has a 155C temperature index that is e to many thermosets. Recognized by UL as UL94V-0 at 0.8mm(0.03in).Information provided by DuPont Performance Polymers物性信息：物理性能额定值 (公制)额定值 (英制)测试方法比重1.79 g/cc1.79 g/ccASTM D792密度1.79 g/cc0.0647 lb/in³ISO 1183填料含量43 %43 %Water Absorption0.060 %@Temperature 23.0 °C0.060 %@Temperature 73.4 °F50%RH,23°C,24h; ASTM D5700.11 %@Temperature 23.0 °C0.11 %@Temperature 73.4 °FE 50%RH; ISO 62, Similar to0.62 %@Temperature 23.0 °C0.62 %@Temperature 73.4 °FSaturation, immersed; ISO 62, Similar to线性成型收缩率0.0013 cm/cm@Thickness 1.57 mm0.0013 in/in@Thickness 0.0618 inFlow0.0020 cm/cm@Thickness 3.20 mm0.0020 in/in@Thickness 0.126 inFlow0.0048 cm/cm@Thickness 1.57 mm0.0048 in/in@Thickness 0.0618 inTransverse0.0065 cm/cm@Thickness 3.20 mm0.0065 in/in@Thickness 0.126 inTransverse线性成型收缩率,Flow0.0025 cm/cm0.0025 in/inAnnealed; ISO 294-40.0020 cm/cm@Thickness 2.00 mm0.0020 in/in@Thickness 0.0787 inISO 294-4线性成型收缩率，横向0.0105 cm/cm0.0105 in/inAnnealed; ISO 294-40.0075 cm/cm@Thickness 2.00 mm0.0075 in/in@Thickness 0.0787 inISO 294-4化合物熔体指数6.0 g/10 min@Load 2.16 kg, Temperature 280 °C6.0 g/10 min@Load 4.76 lb, Temperature 536 °Fcm3/10 min; ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（M 级）9595ASTM DISO 2039/2洛氏硬度（R 级）120120ASTM DISO 2039/2抗张强度(断裂)170 MPa@Temperature 23.0 °C24700 psi@Temperature 73.4 °FISO 527抗张强度55.2 MPa@Temperature 150 °C8010 psi@Temperature 302 °FASTM D63886.5 MPa@Temperature 90.0 °C12500 psi@Temperature 194 °FASTM D638172 MPa@Temperature 23.0 °C24900 psi@Temperature 73.4 °FASTM D638210 MPa@Temperature -40.0 °C30500 psi@Temperature -40.0 °FASTM D63822.4 MPa@Strain 0.470 %, Temperature 150 °C3250 psi@Strain 0.470 %, Temperature 302 °FISO 52727.22 MPa@Strain 0.430 %, Temperature 120 °C3948 psi@Strain 0.430 %, Temperature 248 °FISO 52727.5 MPa@Strain 0.160 %, Temperature 0.000 °C3990 psi@Strain 0.160 %, Temperature 32.0 °FISO 52728.39 MPa@Strain 0.350 %, Temperature 90.0 °C4118 psi@Strain 0.350 %, Temperature 194 °FISO 52729.0 MPa@Strain 0.140 %, Temperature -40.0 °C4210 psi@Strain 0.140 %, Temperature -40.0 °FISO 52730.0 MPa@Strain 0.210 %, Temperature 40.0 °C4350 psi@Strain 0.210 %, Temperature 104 °FISO 52731.0 MPa@Strain 0.180 %, Temperature 23.0 °C4500 psi@Strain 0.180 %, Temperature 73.4 °FISO 52734.9 MPa@Strain 0.940 %, Temperature 150 °C5060 psi@Strain 0.940 %, Temperature 302 °FISO 52735.57 MPa@Strain 0.310 %, Temperature 60.0 °C5159 psi@Strain 0.310 %, Temperature 140 °FISO 52741.5 MPa@Strain 1.41 %, Temperature 150 °C6020 psi@Strain 1.41 %, Temperature 302 °FISO 52741.8 MPa@Strain 0.830 %, Temperature 120 °C6060 psi@Strain 0.830 %, Temperature 248 °FISO 52745.7 MPa@Strain 1.87 %, Temperature 150 °C6630 psi@Strain 1.87 %, Temperature 302 °FISO 52747.19 MPa@Strain 0.690 %, Temperature 90.0 °C6844 psi@Strain 0.690 %, Temperature 194 °FISO 52749.1 MPa@Strain 2.34 %, Temperature 150 °C7120 psi@Strain 2.34 %, Temperature 302 °FISO 52750.35 MPa@Strain 0.370 %, Temperature 40.0 °C7303 psi@Strain 0.370 %, Temperature 104 °FISO 52750.8 MPa@Strain 1.23 %, Temperature 120 °C7370 psi@Strain 1.23 %, Temperature 248 °FISO 52751.7 MPa@Strain 2.81 %, Temperature 150 °C7500 psi@Strain 2.81 %, Temperature 302 °FISO 52752.4 MPa@Strain 0.320 %, Temperature 0.000 °C7600 psi@Strain 0.320 %, Temperature 32.0 °FISO 52753.8 MPa@Strain 3.28 %, Temperature 150 °C7800 psi@Strain 3.28 %, Temperature 302 °FISO 52753.9 MPa@Strain 0.280 %, Temperature -40.0 °C7820 psi@Strain 0.280 %, Temperature -40.0 °FISO 52755.0 MPa@Strain 0.520 %, Temperature 60.0 °C7980 psi@Strain 0.520 %, Temperature 140 °FISO 52755.6 MPa@Strain 3.75 %, Temperature 150 °C8060 psi@Strain 3.75 %, Temperature 302 °FISO 52756.4 MPa@Strain 0.350 %, Temperature 23.0 °C8180 psi@Strain 0.350 %, Temperature 73.4 °FISO 52756.85 MPa@Strain 1.63 %, Temperature 120 °C8245 psi@Strain 1.63 %, Temperature 248 °FISO 52757.1 MPa@Strain 4.21 %, Temperature 150 °C8280 psi@Strain 4.21 %, Temperature 302 °FISO 52758.5 MPa@Strain 4.69 %, Temperature 150 °C8480 psi@Strain 4.69 %, Temperature 302 °FISO 52759.61 MPa@Strain 1.03 %, Temperature 90.0 °C8646 psi@Strain 1.03 %, Temperature 194 °FISO 52761.26 MPa@Strain 2.04 %, Temperature 120 °C8885 psi@Strain 2.04 %, Temperature 248 °FISO 52764.62 MPa@Strain 2.44 %, Temperature 120 °C9372 psi@Strain 2.44 %, Temperature 248 °FISO 52767.28 MPa@Strain 2.84 %, Temperature 120 °C9758 psi@Strain 2.84 %, Temperature 248 °FISO 52768.2 MPa@Strain 1.37 %, Temperature 90.0 °C9890 psi@Strain 1.37 %, Temperature 194 °FISO 52769.36 MPa@Strain 3.24 %, Temperature 120 °C10060 psi@Strain 3.24 %, Temperature 248 °FISO 52771.09 MPa@Strain 3.65 %, Temperature 120 °C10310 psi@Strain 3.65 %, Temperature 248 °FISO 52771.87 MPa@Strain 0.730 %, Temperature 60.0 °C10420 psi@Strain 0.730 %, Temperature 140 °FISO 52772.35 MPa@Strain 4.05 %, Temperature 120 °C10490 psi@Strain 4.05 %, Temperature 248 °FISO 52772.8 MPa@Strain 0.560 %, Temperature 40.0 °C10600 psi@Strain 0.560 %, Temperature 104 °FISO 52774.5 MPa@Strain 0.480 %, Temperature 23.0 °C10800 psi@Strain 0.480 %, Temperature 73.4 °FISO 52774.52 MPa@Strain 1.70 %, Temperature 90.0 °C10810 psi@Strain 1.70 %, Temperature 194 °FISO 52775.5 MPa@Strain 0.420 %, Temperature -40.0 °C11000 psi@Strain 0.420 %, Temperature -40.0 °FISO 52775.9 MPa@Strain 0.470 %, Temperature 0.000 °C11000 psi@Strain 0.470 %, Temperature 32.0 °FISO 52779.34 MPa@Strain 2.04 %, Temperature 90.0 °C11510 psi@Strain 2.04 %, Temperature 194 °FISO 52783.14 MPa@Strain 2.41 %, Temperature 90.0 °C12060 psi@Strain 2.41 %, Temperature 194 °FISO 52783.19 MPa@Strain 0.940 %, Temperature 60.0 °C12070 psi@Strain 0.940 %, Temperature 140 °FISO 52785.76 MPa@Strain 2.75 %, Temperature 90.0 °C12440 psi@Strain 2.75 %, Temperature 194 °FISO 527
