商品描述价格说明联系我们加工级别注塑级、吹塑级牌号RE19045用途级别食品级、汽车部件、板材级、运动器材、瓶盖料、家电部件、电动工具配件、薄壁制品类型标准料是否进口是厂家(产地)美国杜邦特性级别透明级、、耐低温、标准级、耐水解、、耐老化、耐候、抗静电、抗化学性、高强度、高流动、高抗冲、高滑动、高光泽、高刚性销售方式品牌经销产品规格25KG/包产地美国品名美国杜邦PET产品特性阻燃可售卖地全国DuPont Performance Polymers Rynite® RE19045PET (Unverified Data**)Polyethylene Terephthalate (PET), 40% Glass ReinforcedDuPont Performance Polymers产品说明：Rynite® RE19045is a 40% glass and mineral reinforced, flame retardant, polyethylene terephthalate black resin.Information provided by DuPont Performance Polymers物性信息：物理性能额定值 (公制)额定值 (英制)测试方法密度1.73 g/cc0.0625 lb/in³ISO 1183线性成型收缩率,Flow0.0020 cm/cm@Thickness 2.00 mm0.0020 in/in@Thickness 0.0787 inISO 294-4线性成型收缩率，横向0.0090 cm/cm@Thickness 2.00 mm0.0090 in/in@Thickness 0.0787 inISO 294-4化合物熔体指数70 g/10 min@Load 5.00 kg, Temperature 280 °C70 g/10 min@Load 11.0 lb, Temperature 536 °Fcm3/10 min; ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)110 MPa@Temperature 23.0 °C16000 psi@Temperature 73.4 °FISO 527伸长率 (断裂)1.7 %@Temperature 23.0 °C1.7 %@Temperature 73.4 °FISO 527拉伸模量11.0 GPa@Temperature 23.0 °C1600 ksi@Temperature 73.4 °FISO 527弯曲强度170 MPa@Temperature 23.0 °C24700 psi@Temperature 73.4 °FISO 178弯曲模量9.70 GPa@Temperature 23.0 °C1410 ksi@Temperature 73.4 °FISO 178简支梁缺口冲击强度0.650 J/cm²@Temperature 23.0 °C3.09 ft-lb/in²@Temperature 73.4 °FISO 179/1eA电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率5.00e+14 ohm-cm@Temperature 23.0 °C5.00e+14 ohm-cm@Temperature 73.4 °FIEC 60093表面电阻>= 1.00e+15 ohm@Temperature 23.0 °C>= 1.00e+15 ohm@Temperature 73.4 °FIEC 60093介电强度32.0 kV/mm@Temperature 23.0 °C813 kV/in@Temperature 73.4 °FIEC 60243-1热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动500 µm/m-°C@Temperature -40.0 - 23.0 °C278 µin/in-°F@Temperature -40.0 - 73.4 °FISO 11359-1/-2500 µm/m-°C@Temperature 23.0 - 55.0 °C278 µin/in-°F@Temperature 73.4 - 131 °FISO 11359-1/-2500 µm/m-°C@Temperature 55.0 - 160 °C278 µin/in-°F@Temperature 131 - 320 °FISO 11359-1/-2线性热膨胀系数,横向流动61.0 µm/m-°C@Temperature -40.0 - 23.0 °C33.9 µin/in-°F@Temperature -40.0 - 73.4 °FISO 11359-1/-278.0 µm/m-°C@Temperature 23.0 - 55.0 °C43.3 µin/in-°F@Temperature 73.4 - 131 °FISO 11359-1/-2110 µm/m-°C@Temperature 55.0 - 160 °C61.1 µin/in-°F@Temperature 131 - 320 °FISO 11359-1/-2熔融温度247 °C477 °F10°C/min; ISO 11357-1/-3载荷下热变形温度(1.8 MPa)214 °C417 °FISO 75-1/-2玻璃化转变温度，Tg100 °C212 °F10°C/min; ISO 11357-1/-2UL RTI155 °C@Thickness 0.810 mm311 °F@Thickness 0.0319 inUL 746BUL RTI，机械冲击155 °C@Thickness 0.810 mm311 °F@Thickness 0.0319 inUL 746BUL RTI，机械无冲击155 °C@Thickness 0.810 mm311 °F@Thickness 0.0319 inUL 746B可燃性(UL94)V-0@Thickness 0.810 mmV-0@Thickness 0.0319 inUL94加工性能额定值 (公制)额定值 (英制)测试方法加工（熔体）温度270 - 290 °C518 - 554 °F干燥温度120 °C248 °F干燥时间4.00 hour4.00 hour水分含量